Enhanced luminescence properties of low-cost Mn2+ doped willemite based glass–ceramics as potential green phosphor materials
Low-cost Mn2+-doped willemite (α-Zn2SiO4:Mn2+) based glass–ceramics were synthesized by conventional melt–quenching technique using waste soda lime silica (SLS) glasses, zinc oxide (ZnO) and Manganese oxide (MnO) as precursors. The effect of different MnO percentage doping on physical, structural, o...
Saved in:
| Main Authors: | , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Springer
2017
|
| Online Access: | http://psasir.upm.edu.my/id/eprint/61722/1/Enhanced%20luminescence%20properties%20of%20low-cost%20.pdf http://psasir.upm.edu.my/id/eprint/61722/ https://link.springer.com/article/10.1007/s10854-017-7045-9 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Low-cost Mn2+-doped willemite (α-Zn2SiO4:Mn2+) based glass–ceramics were synthesized by conventional melt–quenching technique using waste soda lime silica (SLS) glasses, zinc oxide (ZnO) and Manganese oxide (MnO) as precursors. The effect of different MnO percentage doping on physical, structural, optical and luminescent performance α-Zn2SiO4:Mn2+ based glass–ceramics were comprehensively studies in this work. The presence of α-Zn2SiO4:Mn2+ crystal phase and microstructure was confirmed by X-ray diffraction and field emission scanning electron microscopy spectroscopy. From the Scherrer’s formula, α-Zn2SiO4:Mn2+ have an average crystallite size of 30–40 nm, respectively. Fourier transform infrared reflection spectroscopy displays the structural growth of α-Zn2SiO4:Mn2+ crystal. The green emission centered at about 527 nm from the α-Zn2SiO4:Mn2+ crystal exhibit a resulted from 4T1–6A1 energy transition of Mn2+ ions. Intense emissions of Mn2+ ions at 260 nm excitation were occurs may be caused by the increase of Mn2+ ions into α-Zn2SiO4 crystal structure with lower phonon. Based on the results achieved, this low-cost α-Zn2SiO4:Mn2+ based glass–ceramic exhibit a huge potential to act as a green phosphor in opto-electronic devices. |
|---|