RESIDUAL STRENGTH ANALYSIS OF CORRODED PIPELINE WITH SINGLE DEFECT SUBJECTED TO INTERNAL PRESSURE AND LONGITUDINAL COMPRESSIVE STRESS

Corrosion is a natural phenomenon which causes the destruction and deterioration of material because of its reaction with the environment. Corrosion can be either general or localised corrosion. The corroded pipeline will lead to the failure of the pipeline. Pipeline failure may cause major losse...

Full description

Saved in:
Bibliographic Details
Main Author: ISMAIL, MOHAMED HAKAM HUSAIRI
Format: Final Year Project
Language:English
Published: IRC 2016
Subjects:
TJ Mechanical engineering and machinery
Online Access:http://utpedia.utp.edu.my/17368/1/HARDBOUND%20HAKAM%20HUSAIRI.pdf
http://utpedia.utp.edu.my/17368/
Tags: Add Tag
No Tags, Be the first to tag this record!
id my-utp-utpedia.17368
record_format eprints
spelling my-utp-utpedia.173682017-11-15T09:56:11Z http://utpedia.utp.edu.my/17368/ RESIDUAL STRENGTH ANALYSIS OF CORRODED PIPELINE WITH SINGLE DEFECT SUBJECTED TO INTERNAL PRESSURE AND LONGITUDINAL COMPRESSIVE STRESS ISMAIL, MOHAMED HAKAM HUSAIRI TJ Mechanical engineering and machinery Corrosion is a natural phenomenon which causes the destruction and deterioration of material because of its reaction with the environment. Corrosion can be either general or localised corrosion. The corroded pipeline will lead to the failure of the pipeline. Pipeline failure may cause major losses to the environment and also could lead to fatality of human lives. The integrity of pipeline is an essential aspect that had to be considered in order to avoid unnecessary losses or accidents during operation. The current available codes are said to be conservative which lead to premature repair or replacement. The objective of this study is to estimate the failure pressure of corroded pipeline with single defect subjected to internal pressure and longitudinal compressive stress. This study was focussed on API 5L X52 material. The failure pressure results obtained by the Finite Element Analysis (FEA) were compared to the results obtained using DNV – RP – F101 standards. IRC 2016-09 Final Year Project NonPeerReviewed application/pdf en http://utpedia.utp.edu.my/17368/1/HARDBOUND%20HAKAM%20HUSAIRI.pdf ISMAIL, MOHAMED HAKAM HUSAIRI (2016) RESIDUAL STRENGTH ANALYSIS OF CORRODED PIPELINE WITH SINGLE DEFECT SUBJECTED TO INTERNAL PRESSURE AND LONGITUDINAL COMPRESSIVE STRESS. IRC, Universiti Teknologi PETRONAS. (Submitted)
institution Universiti Teknologi Petronas
building UTP Resource Centre
collection Institutional Repository
continent Asia
country Malaysia
content_provider Universiti Teknologi Petronas
content_source UTP Electronic and Digitized Intellectual Asset
url_provider http://utpedia.utp.edu.my/
language English
topic TJ Mechanical engineering and machinery
spellingShingle TJ Mechanical engineering and machinery
ISMAIL, MOHAMED HAKAM HUSAIRI
RESIDUAL STRENGTH ANALYSIS OF CORRODED PIPELINE WITH SINGLE DEFECT SUBJECTED TO INTERNAL PRESSURE AND LONGITUDINAL COMPRESSIVE STRESS
description Corrosion is a natural phenomenon which causes the destruction and deterioration of material because of its reaction with the environment. Corrosion can be either general or localised corrosion. The corroded pipeline will lead to the failure of the pipeline. Pipeline failure may cause major losses to the environment and also could lead to fatality of human lives. The integrity of pipeline is an essential aspect that had to be considered in order to avoid unnecessary losses or accidents during operation. The current available codes are said to be conservative which lead to premature repair or replacement. The objective of this study is to estimate the failure pressure of corroded pipeline with single defect subjected to internal pressure and longitudinal compressive stress. This study was focussed on API 5L X52 material. The failure pressure results obtained by the Finite Element Analysis (FEA) were compared to the results obtained using DNV – RP – F101 standards.
format Final Year Project
author ISMAIL, MOHAMED HAKAM HUSAIRI
author_facet ISMAIL, MOHAMED HAKAM HUSAIRI
author_sort ISMAIL, MOHAMED HAKAM HUSAIRI
title RESIDUAL STRENGTH ANALYSIS OF CORRODED PIPELINE WITH SINGLE DEFECT SUBJECTED TO INTERNAL PRESSURE AND LONGITUDINAL COMPRESSIVE STRESS
title_short RESIDUAL STRENGTH ANALYSIS OF CORRODED PIPELINE WITH SINGLE DEFECT SUBJECTED TO INTERNAL PRESSURE AND LONGITUDINAL COMPRESSIVE STRESS
title_full RESIDUAL STRENGTH ANALYSIS OF CORRODED PIPELINE WITH SINGLE DEFECT SUBJECTED TO INTERNAL PRESSURE AND LONGITUDINAL COMPRESSIVE STRESS
title_fullStr RESIDUAL STRENGTH ANALYSIS OF CORRODED PIPELINE WITH SINGLE DEFECT SUBJECTED TO INTERNAL PRESSURE AND LONGITUDINAL COMPRESSIVE STRESS
title_full_unstemmed RESIDUAL STRENGTH ANALYSIS OF CORRODED PIPELINE WITH SINGLE DEFECT SUBJECTED TO INTERNAL PRESSURE AND LONGITUDINAL COMPRESSIVE STRESS
title_sort residual strength analysis of corroded pipeline with single defect subjected to internal pressure and longitudinal compressive stress
publisher IRC
publishDate 2016
url http://utpedia.utp.edu.my/17368/1/HARDBOUND%20HAKAM%20HUSAIRI.pdf
http://utpedia.utp.edu.my/17368/
_version_ 1739832375926325248
score 13.211869

Similar Items