Luminescence properties of cerium doped iron calcium boroaluminate glass
Borate glass system of composition (100-x)B2O3-15Al2O3-20CaO-0.4Fe2O3-xCeO2 with x = 0, 0.25, 0.50, 0.75, and 1.0 mol% were prepared using conventional melt-quenching method. Optical measurements were carried out at room temperature to determine the Cerium (Ce3+) ions concentration dependent absorpt...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Conference or Workshop Item |
| Published: |
2017
|
| Subjects: | |
| Online Access: | http://eprints.utm.my/id/eprint/97349/ http://dx.doi.org/10.4028/www.scientific.net/SSP.268.72 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Borate glass system of composition (100-x)B2O3-15Al2O3-20CaO-0.4Fe2O3-xCeO2 with x = 0, 0.25, 0.50, 0.75, and 1.0 mol% were prepared using conventional melt-quenching method. Optical measurements were carried out at room temperature to determine the Cerium (Ce3+) ions concentration dependent absorption and luminescence emission properties of such glass system. Optical energy band gap of the glass system were evaluated as a function of Ce3+ ions content. Indirect band gap energy was found to be lower than the direct band gap energy. Urbach energy was ranged between 0.12-0.17 eV. An increased broad absorption is observed in the UV region with increasing Ce3+ ions concentration. The emission spectra of the glass system recorded with 380 nm excitation wavelength revealed prominent cyan-green emission. |
|---|