Investigation of tribological properties of CuO/palm oil nanolubricant using pin-on-disc tribotester
It has been proposed that nanoparticles have the ability to enhance the tribological properties of lubricants. In the present research, the tribological properties of a palm-oil-based nanolubricant with copper (II) oxide (CuO) nanoparticles have been investigated experimentally using a pin-on-disc t...
保存先:
| 主要な著者: | , , |
|---|---|
| フォーマット: | 論文 |
| 言語: | English |
| 出版事項: |
ICE Publishing
2018
|
| 主題: | |
| オンライン･アクセス: | http://eprints.utm.my/id/eprint/85422/1/NurulFarhanahAzman2018_InvestigationofTribologicalPropertiesofCuO.pdf http://eprints.utm.my/id/eprint/85422/ http://dx.doi.org/10.1680/jgrma.17.00026 |
| タグ: |
タグ追加
タグなし, このレコードへの初めてのタグを付けませんか!
|
| 要約: | It has been proposed that nanoparticles have the ability to enhance the tribological properties of lubricants. In the present research, the tribological properties of a palm-oil-based nanolubricant with copper (II) oxide (CuO) nanoparticles have been investigated experimentally using a pin-on-disc tribotester. The experiments were conducted at a sliding speed of 0·2m/s and an applied load of 9·8 N, which corresponds to a contact pressure of 0·93GPa for 60min duration. Commercial mineral oil (SAE40) was used for comparison purposes. The results show that the tribological properties of the palm-oilbased lubricant were improved with the presence of copper (II) oxide nanoparticles, showing huge reductions in coefficient of friction and wear scar diameter of about 56 and 48%, respectively. The findings revealed that the presence of copper (II) oxide in palm kernel oil (PKO) reduced the roughness of the pin surface by 43·7%. The results also show that the tribological properties of the copper (II) oxide/palm-oil-based nanolubricant were comparable to those of SAE40. |
|---|