Effect of intermediate layer on gas separation performance of disk supported carbon membrane
Porous alumina disk ceramic was decorated with various types of intermediate layers via one-step spray coating-carbonization technique. P-84 (BTDA-TDI/MDI) polymeric solution was sprayed on the alumina disk with an incorporation of intermediate layer. The membrane was carbonized at 700°C under nitro...
Saved in:
| Main Authors: | , , , , , , |
|---|---|
| Format: | Conference or Workshop Item |
| Published: |
2018
|
| Subjects: | |
| Online Access: | http://eprints.utm.my/id/eprint/82439/ http://dx.doi.org/10.1080/01496395.2017.1321671 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Porous alumina disk ceramic was decorated with various types of intermediate layers via one-step spray coating-carbonization technique. P-84 (BTDA-TDI/MDI) polymeric solution was sprayed on the alumina disk with an incorporation of intermediate layer. The membrane was carbonized at 700°C under nitrogen (N2) atmosphere with a heating rate of 3°C/min. The resultant carbon membrane was characterized in terms of its thermal stability, structural morphology, and gas permeation properties. A high-performance carbon membrane was obtained with the intermediate layer of the alumina powder, which exhibited the best selectivity of O2/N2, CO2/N2 and CO2/CH4 of 4.39, 19.89 and 58.43, respectively. |
|---|