Quasi-Static flexural and indentation behaviour of polymer-metal laminate
Metal-polymer laminates were subjected to quasi-static flexural and indentation loading. The laminates were made of two aluminium skins heat-bonded (laminated) to a core made of polyethylene plastic material. The samples were trimmed into standard-sized beams and panels which were then tested in fle...
保存先:
| 主要な著者: | , , , |
|---|---|
| フォーマット: | 論文 |
| 出版事項: |
Trans Tech Publications
2014
|
| 主題: | |
| オンライン･アクセス: | http://eprints.utm.my/id/eprint/62381/ http://dx.doi.org/10.4028/www.scientific.net/AMR.970.88 |
| タグ: |
タグ追加
タグなし, このレコードへの初めてのタグを付けませんか!
|
| 要約: | Metal-polymer laminates were subjected to quasi-static flexural and indentation loading. The laminates were made of two aluminium skins heat-bonded (laminated) to a core made of polyethylene plastic material. The samples were trimmed into standard-sized beams and panels which were then tested in flexural and indentation using the Instron universal testing machine at loading rates of 1 mm/min, 10 mm/min and 100 mm/min. The load-displacement and energy absorption curves of the composite beams were recorded. It was found that the loading rate has a large effect on flexural and indentation behaviour of aluminium composite laminate. |
|---|