Effects of complexing Agents on three Steps pulse Electrodeposited SnS thin films
SnS thin films were prepared on indium-tin-oxide (ITO)-coated glass substrate at room temperature via three steps pulse electrodeposition from an aqueous bath containing 30 mM SnSO4 and 100 mM Na2S2O3. The effects of two complexing agents, i.e., ethylenediaminetetraacetic (acid-EDTA [CH2N(CH2COOH)2]...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Published: |
Elsevier Ltd
2015
|
| Subjects: | |
| Online Access: | http://eprints.utm.my/id/eprint/58417/ http://dx.doi.org/10.1016/j.mssp.2015.04.028 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | SnS thin films were prepared on indium-tin-oxide (ITO)-coated glass substrate at room temperature via three steps pulse electrodeposition from an aqueous bath containing 30 mM SnSO4 and 100 mM Na2S2O3. The effects of two complexing agents, i.e., ethylenediaminetetraacetic (acid-EDTA [CH2N(CH2COOH)2]2) and L(+)-tartaric acid (C4H6O6) under different concentration were studied. All the deposited samples exhibited p-type conductivity behaviour. The films deposited with the complexing agents generally showed less oxygen content and larger sulfur content than those deposited without the agents. The film thickness was decreased by addition of EDTA and low concentration of tartaric acid (<10 mM), while it was slightly increased with a large amount of tartaric acid (>30 mM). Larger crystalline size and larger optical transmission were observed for SnS deposited with tartaric acid concentration larger than 30 mM. |
|---|