Surface modification of thin film nanocomposite membranes using plasma enhanced chemical vapor deposition method for desalination process

Thin film composite reverse osmosis (TFC RO) membrane has been commercially used to desalinate salty water since the 1970s to produce clean water to address water scarcity issue in many countries. However, the commercial TFC RO membranes are still associated with several drawbacks including permeabi...

Full description

Saved in:
Bibliographic Details
Main Author: Khoo, Ying Siew
Format: Thesis
Language:English
Published: 2021
Subjects:
Q Science (General)
Online Access:http://eprints.utm.my/id/eprint/102027/1/KhooYingSiewPSChE2021.pdf
http://eprints.utm.my/id/eprint/102027/
http://dms.library.utm.my:8080/vital/access/manager/Repository/vital:145663
Tags: Add Tag
No Tags, Be the first to tag this record!
id my.utm.102027
record_format eprints
spelling my.utm.1020272023-07-31T07:08:15Z http://eprints.utm.my/id/eprint/102027/ Surface modification of thin film nanocomposite membranes using plasma enhanced chemical vapor deposition method for desalination process Khoo, Ying Siew Q Science (General) Thin film composite reverse osmosis (TFC RO) membrane has been commercially used to desalinate salty water since the 1970s to produce clean water to address water scarcity issue in many countries. However, the commercial TFC RO membranes are still associated with several drawbacks including permeability/selectivity trade-off and scaling problem. Thin film nanocomposite (TFN) membrane incorporating titania nanotube (TNT) as previously reported, was found to offer outstanding features as the incorporation of TNT in polyamide (PA) layer could improve membrane pure water flux (PWF) and salt separation performance. However, TNT tends to have high aggregation ability and low dispersion in the organic solvent, which reduces its practicability for TFN membrane development. Therefore, this study aimed to develop a new type of TFN membrane incorporated with TNT functionalized using an environmentally friendly plasma-enhanced chemical vapour deposition (PECVD) method. The surface of TNT was respectively functionalized with 2-hydroxyethyl methacrylate (HEMA) and methyl methacrylate (MMA) at different plasma deposition times (5 and 10 min). Results showed that the incorporation of 0.05 w/v% MMA-modified TNT (5 min) into the membrane outperformed the HEMA-modified TNT (5 min) with respect to PWF and NaCl rejection, achieving 52.5 L/m2.h (measured at 15 bar) and 97.6% (tested at 2000 ppm NaCl feed solution at 15 bar), respectively. This is due to the even distribution of MMA-modified TNT throughout the PA layer which increased the membrane water affinity. The TFN membrane incorporated with MMA-modified TNT was further coated using hydrophilic acrylic acid (AA) via PECVD method as a strategy to heal the surface defects of the selective layer caused by TNT incorporation. The NaCl passage was observed to reduce from 2.43% to 1.50% (tested at 2000 ppm NaCl feed solution at 15 bar) without significantly altering PWF. This membrane also exhibited extraordinary anti-scaling performance with a higher flux recovery rate (FRR) (>85%) compared to the unmodified TFC membrane (74.8%), which is mainly attributed to its enhanced surface negative charge and improved hydrophilicity. Likewise, the developed AA-modified TFN membrane could effectively mitigate the silica scaling by achieving higher FRR (88.1%) than the unmodified membranes. In conclusion, this work demonstrated the potential of using PECVD method to rapidly modify not only the surface properties of nanomaterials but also the top PA selective layer of TFN membranes, overcoming the drawbacks associated with the TFC membrane and improving the TFN membrane for enhanced salt rejection and anti-scaling performance without trading-off its water permeability. 2021 Thesis NonPeerReviewed application/pdf en http://eprints.utm.my/id/eprint/102027/1/KhooYingSiewPSChE2021.pdf Khoo, Ying Siew (2021) Surface modification of thin film nanocomposite membranes using plasma enhanced chemical vapor deposition method for desalination process. PhD thesis, Universiti Teknologi Malaysia, Faculty of Engineering - School of Chemical & Energy Engineering. http://dms.library.utm.my:8080/vital/access/manager/Repository/vital:145663
institution Universiti Teknologi Malaysia
building UTM Library
collection Institutional Repository
continent Asia
country Malaysia
content_provider Universiti Teknologi Malaysia
content_source UTM Institutional Repository
url_provider http://eprints.utm.my/
language English
topic Q Science (General)
spellingShingle Q Science (General)
Khoo, Ying Siew
Surface modification of thin film nanocomposite membranes using plasma enhanced chemical vapor deposition method for desalination process
description Thin film composite reverse osmosis (TFC RO) membrane has been commercially used to desalinate salty water since the 1970s to produce clean water to address water scarcity issue in many countries. However, the commercial TFC RO membranes are still associated with several drawbacks including permeability/selectivity trade-off and scaling problem. Thin film nanocomposite (TFN) membrane incorporating titania nanotube (TNT) as previously reported, was found to offer outstanding features as the incorporation of TNT in polyamide (PA) layer could improve membrane pure water flux (PWF) and salt separation performance. However, TNT tends to have high aggregation ability and low dispersion in the organic solvent, which reduces its practicability for TFN membrane development. Therefore, this study aimed to develop a new type of TFN membrane incorporated with TNT functionalized using an environmentally friendly plasma-enhanced chemical vapour deposition (PECVD) method. The surface of TNT was respectively functionalized with 2-hydroxyethyl methacrylate (HEMA) and methyl methacrylate (MMA) at different plasma deposition times (5 and 10 min). Results showed that the incorporation of 0.05 w/v% MMA-modified TNT (5 min) into the membrane outperformed the HEMA-modified TNT (5 min) with respect to PWF and NaCl rejection, achieving 52.5 L/m2.h (measured at 15 bar) and 97.6% (tested at 2000 ppm NaCl feed solution at 15 bar), respectively. This is due to the even distribution of MMA-modified TNT throughout the PA layer which increased the membrane water affinity. The TFN membrane incorporated with MMA-modified TNT was further coated using hydrophilic acrylic acid (AA) via PECVD method as a strategy to heal the surface defects of the selective layer caused by TNT incorporation. The NaCl passage was observed to reduce from 2.43% to 1.50% (tested at 2000 ppm NaCl feed solution at 15 bar) without significantly altering PWF. This membrane also exhibited extraordinary anti-scaling performance with a higher flux recovery rate (FRR) (>85%) compared to the unmodified TFC membrane (74.8%), which is mainly attributed to its enhanced surface negative charge and improved hydrophilicity. Likewise, the developed AA-modified TFN membrane could effectively mitigate the silica scaling by achieving higher FRR (88.1%) than the unmodified membranes. In conclusion, this work demonstrated the potential of using PECVD method to rapidly modify not only the surface properties of nanomaterials but also the top PA selective layer of TFN membranes, overcoming the drawbacks associated with the TFC membrane and improving the TFN membrane for enhanced salt rejection and anti-scaling performance without trading-off its water permeability.
format Thesis
author Khoo, Ying Siew
author_facet Khoo, Ying Siew
author_sort Khoo, Ying Siew
title Surface modification of thin film nanocomposite membranes using plasma enhanced chemical vapor deposition method for desalination process
title_short Surface modification of thin film nanocomposite membranes using plasma enhanced chemical vapor deposition method for desalination process
title_full Surface modification of thin film nanocomposite membranes using plasma enhanced chemical vapor deposition method for desalination process
title_fullStr Surface modification of thin film nanocomposite membranes using plasma enhanced chemical vapor deposition method for desalination process
title_full_unstemmed Surface modification of thin film nanocomposite membranes using plasma enhanced chemical vapor deposition method for desalination process
title_sort surface modification of thin film nanocomposite membranes using plasma enhanced chemical vapor deposition method for desalination process
publishDate 2021
url http://eprints.utm.my/id/eprint/102027/1/KhooYingSiewPSChE2021.pdf
http://eprints.utm.my/id/eprint/102027/
http://dms.library.utm.my:8080/vital/access/manager/Repository/vital:145663
_version_ 1773543494182240256
score 13.211869

Similar Items