The strain-rate and temperature dependence of the mechanical properties of polyetherketone and polyetheretherketone
ABSTRACT The mechanical properties of polyetheretherketone and polyetherketone were studied as a function of strain rate and temperature in the ranges 10⁻3 to 103s⁻1 and 20–200°C. At temperatures below the glass transition temperature, Tg, the strain-rate sensitivity of both polymers was found to be...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Springer
1996
|
| Online Access: | http://psasir.upm.edu.my/id/eprint/39688/1/3.%20The%20strain-rate%20and%20temperature%20dependence%20of%20the%20mechanical%20properties%20of%20polyetherketone%20and%20polyetheretherketone.pdf http://psasir.upm.edu.my/id/eprint/39688/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | ABSTRACT The mechanical properties of polyetheretherketone and polyetherketone were studied as a function of strain rate and temperature in the ranges 10⁻3 to 103s⁻1 and 20–200°C. At temperatures below the glass transition temperature, Tg, the strain-rate sensitivity of both polymers was found to be almost independent of temperature with a value of ̴4 MPa per decade of strain rate and the behaviour was well described by an Eyring relationship leading to an activation volume of ̴1 nm3. Above Tg, X-ray and differential scanning calorimetry studies show that cold-crystallization phenomena play a very important part in the polymer behaviour, leading to an increase of yield stress with increasing temperature. The crystallization was found to be highly strain-rate dependent with no increase in crystalline content occurring in quasi-static tests and increases of up to 20% in higher rate tests. Much of the data have been gathered using novel test equipment which is described in the paper. |
|---|