Surface characteristics of electrospun p-sulphonated calix[4]Arene functionalized cellulose acetate nanofiber and its behaviour towards methylene blue adsorption
p-sulphonated calix[4]arene (p-SOCX) functionalized cellulose acetate/graphene oxide (CA/GO) nanofibers were successfully prepared via the electrospinning technique. The presence of p-SOCX within the fiber matrix was ascertained using Fourier Transform Infrared spectroscopy and Carbon-Hydrogen-Nitro...
保存先:
| 主要な著者: | , , , , |
|---|---|
| フォーマット: | 論文 |
| 出版事項: |
Hindawi
2022
|
| オンライン･アクセス: | http://psasir.upm.edu.my/id/eprint/103366/ https://www.hindawi.com/journals/ast/2022/4659410/ |
| タグ: |
タグ追加
タグなし, このレコードへの初めてのタグを付けませんか!
|
| 要約: | p-sulphonated calix[4]arene (p-SOCX) functionalized cellulose acetate/graphene oxide (CA/GO) nanofibers were successfully prepared via the electrospinning technique. The presence of p-SOCX within the fiber matrix was ascertained using Fourier Transform Infrared spectroscopy and Carbon-Hydrogen-Nitrogen-Sulphur elemental analyses. Apparent changes in morphology of the samples were observed under scanning electron microscope where fiber diameters increased with increasing p-SOCX content. Preliminary dye removal test at different pH, dosage, and temperature of functionalized CA/GO nanofiber demonstrates enhanced adsorption capacity of methylene blue in presence of p-SOCX compared to pristine CA nanofiber and CA/GO nanofiber at an optimum pH 8. The highest removal efficiency obtained was 88.84% with initial methylene blue dye concentration of 10 mg/L, adsorbent dosage of 20 mg/10 mL, contact time of 30 min at room temperature ca. 293 K. |
|---|