To study the fatigue crack growth in welded steel

This study investigates fatigue crack growth of two type welding subjected HAZ (Heat Affected Zone), Porosity, Slag Inclusion. Metal weld were produced in 5mm thick A516 GRADE 70 plates with a single "V" without post-weld treatment. A Tensile test was used to both type of welding. Liquid P...

Full description

Saved in:
Bibliographic Details
Main Author: Thines Murugan
Format: text::Thesis
Language:English
Published: 2023
Subjects:
Tags: Add Tag
No Tags, Be the first to tag this record!
id my.uniten.dspace-20948
record_format dspace
spelling my.uniten.dspace-209482023-05-04T13:23:58Z To study the fatigue crack growth in welded steel Thines Murugan Materials -- Fatigue Steel -- Fatigue Steel fracture This study investigates fatigue crack growth of two type welding subjected HAZ (Heat Affected Zone), Porosity, Slag Inclusion. Metal weld were produced in 5mm thick A516 GRADE 70 plates with a single "V" without post-weld treatment. A Tensile test was used to both type of welding. Liquid Penetrant test were conducted under room temperature to identify crack within the welding joint of SMAW and MIG. Microstructure Testing were used under magnification of 500x to identify the fatigue crack growth. Radiographic film test were conducted in X-rays emission to identify inner crack growth and type of growth within SMAW and MIG type of welding. 2023-05-03T15:37:59Z 2023-05-03T15:37:59Z 2015 Resource Types::text::Thesis https://irepository.uniten.edu.my/handle/123456789/20948 en application/pdf
institution Universiti Tenaga Nasional
building UNITEN Library
collection Institutional Repository
continent Asia
country Malaysia
content_provider Universiti Tenaga Nasional
content_source UNITEN Institutional Repository
url_provider http://dspace.uniten.edu.my/
language English
topic Materials -- Fatigue
Steel -- Fatigue
Steel fracture
spellingShingle Materials -- Fatigue
Steel -- Fatigue
Steel fracture
Thines Murugan
To study the fatigue crack growth in welded steel
description This study investigates fatigue crack growth of two type welding subjected HAZ (Heat Affected Zone), Porosity, Slag Inclusion. Metal weld were produced in 5mm thick A516 GRADE 70 plates with a single "V" without post-weld treatment. A Tensile test was used to both type of welding. Liquid Penetrant test were conducted under room temperature to identify crack within the welding joint of SMAW and MIG. Microstructure Testing were used under magnification of 500x to identify the fatigue crack growth. Radiographic film test were conducted in X-rays emission to identify inner crack growth and type of growth within SMAW and MIG type of welding.
format Resource Types::text::Thesis
author Thines Murugan
author_facet Thines Murugan
author_sort Thines Murugan
title To study the fatigue crack growth in welded steel
title_short To study the fatigue crack growth in welded steel
title_full To study the fatigue crack growth in welded steel
title_fullStr To study the fatigue crack growth in welded steel
title_full_unstemmed To study the fatigue crack growth in welded steel
title_sort to study the fatigue crack growth in welded steel
publishDate 2023
_version_ 1806423521098727424
score 13.222552