Study of erosion corrosion in oil and gas industry

This project is about study of the erosion corrosion in oil and gas industries based on the samples from Petronas Gas Processing Plant. The microstructure and hardness analysis was done to the sample ASTM A 105 Carbon Steel (elbow that failed due to erosion corrosion). Found that the microstructure...

全面介绍

Saved in:
书目详细资料
主要作者: Hasyim Salleh
其他作者: Nazree Derman, Dr. (Advisor)
格式:
语言:English
出版: Universiti Malaysia Perlis 2009
主题:
Corrosion and anti-corrosives
Metals > Erosion
Erosion
Carbon steel > Thermal properties
Carbon steel > Corrosion
在线阅读:http://dspace.unimap.edu.my/xmlui/handle/123456789/4856
标签: 添加标签
没有标签, 成为第一个标记此记录!
id my.unimap-4856
record_format dspace
spelling my.unimap-48562009-03-02T08:12:20Z Study of erosion corrosion in oil and gas industry Hasyim Salleh Nazree Derman, Dr. (Advisor) Corrosion and anti-corrosives Metals -- Erosion Erosion Carbon steel -- Thermal properties Carbon steel -- Corrosion This project is about study of the erosion corrosion in oil and gas industries based on the samples from Petronas Gas Processing Plant. The microstructure and hardness analysis was done to the sample ASTM A 105 Carbon Steel (elbow that failed due to erosion corrosion). Found that the microstructure and hardness of failed samples was altered and different compared to new sample (with same grade of carbon steel). Experiment on erosion corrosion was design in order to get more understanding on erosion corrosion mechanism. Result of experiment shown weight loss of the sample is 6 grams for 37 hours experiment. In order to measured corrosion rate of the sample, tafel plot (electrochemical techniques of corrosion measurement) was run by using Gamry Instruments. From data gathered, the corrosion rate of ASTM A 105 carbon steel in Sodium Chloride environment is 3.070682E-03 millimeter per year (mm/year). 2009-03-02T08:12:20Z 2009-03-02T08:12:20Z 2008-05 http://hdl.handle.net/123456789/4856 en Universiti Malaysia Perlis School of Materials Engineering
institution Universiti Malaysia Perlis
building UniMAP Library
collection Institutional Repository
continent Asia
country Malaysia
content_provider Universiti Malaysia Perlis
content_source UniMAP Library Digital Repository
url_provider http://dspace.unimap.edu.my/
language English
topic Corrosion and anti-corrosives
Metals -- Erosion
Erosion
Carbon steel -- Thermal properties
Carbon steel -- Corrosion
spellingShingle Corrosion and anti-corrosives
Metals -- Erosion
Erosion
Carbon steel -- Thermal properties
Carbon steel -- Corrosion
Hasyim Salleh
Study of erosion corrosion in oil and gas industry
description This project is about study of the erosion corrosion in oil and gas industries based on the samples from Petronas Gas Processing Plant. The microstructure and hardness analysis was done to the sample ASTM A 105 Carbon Steel (elbow that failed due to erosion corrosion). Found that the microstructure and hardness of failed samples was altered and different compared to new sample (with same grade of carbon steel). Experiment on erosion corrosion was design in order to get more understanding on erosion corrosion mechanism. Result of experiment shown weight loss of the sample is 6 grams for 37 hours experiment. In order to measured corrosion rate of the sample, tafel plot (electrochemical techniques of corrosion measurement) was run by using Gamry Instruments. From data gathered, the corrosion rate of ASTM A 105 carbon steel in Sodium Chloride environment is 3.070682E-03 millimeter per year (mm/year).
author2 Nazree Derman, Dr. (Advisor)
author_facet Nazree Derman, Dr. (Advisor)
Hasyim Salleh
format
author Hasyim Salleh
author_sort Hasyim Salleh
title Study of erosion corrosion in oil and gas industry
title_short Study of erosion corrosion in oil and gas industry
title_full Study of erosion corrosion in oil and gas industry
title_fullStr Study of erosion corrosion in oil and gas industry
title_full_unstemmed Study of erosion corrosion in oil and gas industry
title_sort study of erosion corrosion in oil and gas industry
publisher Universiti Malaysia Perlis
publishDate 2009
url http://dspace.unimap.edu.my/xmlui/handle/123456789/4856
_version_ 1643788255106170880
score 13.252575

相似书籍