Tensile properties of alkali treated sugar palm fiber
A study of the effect of alkaline treatment on the tensile properties of sugar palm fiber.The fiber were treated using sodium hydroxide (NaOH) with 2%, 4% and 6% concentration solution for 1 hour soaking time. The purpose of treating fiber with alkali was to enhance the tensile strength and young mo...
Saved in:
| 主要作者: | |
|---|---|
| 格式: | Undergraduates Project Papers |
| 語言: | English English English |
| 出版: |
2013
|
| 主題: | |
| 在線閱讀: | http://umpir.ump.edu.my/id/eprint/8486/1/CD7974_%40_39.pdf http://umpir.ump.edu.my/id/eprint/8486/4/1.pdf http://umpir.ump.edu.my/id/eprint/8486/5/3.pdf http://umpir.ump.edu.my/id/eprint/8486/ |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | A study of the effect of alkaline treatment on the tensile properties of sugar palm fiber.The fiber were treated using sodium hydroxide (NaOH) with 2%, 4% and 6% concentration solution for 1 hour soaking time. The purpose of treating fiber with alkali was to enhance the tensile strength and young modulus of single sugar palm fiber. The maximum tensile strength for untreated fiber is 63.05 MPa.The maximum tensile strength for occurred at 2% NaOH solution with 1 hour of soaking time, i.e 67.85 MPa. But, the maximum fiber for treated 4% NaOH solution with 1 hour of soaking time is 76.37MPa and for fiber treated 6% NaOH solution is 82.13 MPa. |
|---|