Performance of ethyl vinyl acetate or low density polyethylene or nano magnesium hydroxide via ultrasonic compounding / Illy Athira Azman
The effects of nano-MH loading on mechanical and thermal properties of EVA/LDPE/nano-MH at different ultrasonic frequency were studied. The best formulation was selected based on the distribution of nano-MH loading and ultrasonic frequency. A range of nano-MH loading which is from 0 pph to maximum o...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2019
|
| Online Access: | https://ir.uitm.edu.my/id/eprint/87942/1/87942.pdf https://ir.uitm.edu.my/id/eprint/87942/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | The effects of nano-MH loading on mechanical and thermal properties of EVA/LDPE/nano-MH at different ultrasonic frequency were studied. The best formulation was selected based on the distribution of nano-MH loading and ultrasonic frequency. A range of nano-MH loading which is from 0 pph to maximum of 20 pph with ultrasonic extrusion 0 kHz, 50 kHz and 100 kHz frequencies have been used in order to improve the mechanical and thermal properties as well as flame retardancy ability. It was found that, 10 pph of nano loading with 100 kHz ultrasonic assisted has greater mechanical properties compared to the nanocomposite without ultrasonication. Further increased of nano-MH loading, decreased the mechanical properties. |
|---|