The aqueous environmental effects on Co-Ni-Fe coated stainless steel bolts / Muhammad Syafiq Md.Nor

Stainless steel 304 (SS304) is one of the widely used steel fasteners in both commercial and industrial sectors. However, stainless steel is susceptible to failure in a harsh corrosive environment despite its good corrosion resistance. Nowadays, the electrodeposition process is gaining traction as a...

Full description

Saved in:
Bibliographic Details
Main Author: Md. Nor, Muhammad Syafiq
Format: Thesis
Language:English
Published: 2022
Subjects:
Physical properties
Metals
Online Access:https://ir.uitm.edu.my/id/eprint/77964/1/77964.pdf
https://ir.uitm.edu.my/id/eprint/77964/
Tags: Add Tag
No Tags, Be the first to tag this record!
id my.uitm.ir.77964
record_format eprints
spelling my.uitm.ir.779642023-05-29T07:35:08Z https://ir.uitm.edu.my/id/eprint/77964/ The aqueous environmental effects on Co-Ni-Fe coated stainless steel bolts / Muhammad Syafiq Md.Nor Md. Nor, Muhammad Syafiq Physical properties Metals Stainless steel 304 (SS304) is one of the widely used steel fasteners in both commercial and industrial sectors. However, stainless steel is susceptible to failure in a harsh corrosive environment despite its good corrosion resistance. Nowadays, the electrodeposition process is gaining traction as a flexible method to improve surface properties using various types of alloys. In this study, Co-Ni-Fe alloy was chosen as a protective coating for SS304 bolts through electrodeposition process. The purposes of this research are to develop a better understanding on the surface properties of Co-Ni-Fe thin film deposited onto stainless steel 304 bolt and the corrosion behaviour in corrosive mediums taken from actual environments. First, the coatings were synthesised with deposition time of 15, 30, and 45 minutes and current density of 28, 35, and 42 mA/cm2 whereas the other plating parameters were kept constant. The samples were characterised using scanning electron microscope (surface morphology and elemental composition), 3D surface metrology system (roughness and thickness), and hardness testing machine (microhardness). In most cases, there was a correlation between the trends of surface roughness and corrosion rate. Both properties had lower values as deposition time increased. In order to select the best combination of plating parameters for environmental tests, the samples were further analysed with potentiodynamic polarisation technique using a potentiostat to obtain the corrosion rates. The optimum plating parameters were 30 minutes and 42 mA/cm2 because the corrosion rate was the lowest. More samples were produced using these optimum parameters for the environmental immersion test, which consisted of river water, tap water and seawater. River water was the most aggressive environment because the samples lost the highest weight followed by seawater and tap water during the weight loss analysis. Electrochemical impedance spectroscopy (EIS) results indicated that the impedance |Z| value varied as immersion period increase. River and tap water had an increasing |Z| value whereas seawater had a decreasing |Z| value over times. In terms of electrochemical aspects, river water caused the highest corrosion rate whereas the weight loss test showed that seawater caused the highest corrosion rate. It did not had direct relationship with weight loss trend. Based on these environmental tests, the corrosion resistance of Co-Ni-Fe coating is the highest in tap water, followed by river water and seawater. 2022 Thesis NonPeerReviewed text en https://ir.uitm.edu.my/id/eprint/77964/1/77964.pdf The aqueous environmental effects on Co-Ni-Fe coated stainless steel bolts / Muhammad Syafiq Md.Nor. (2022) Masters thesis, thesis, Universiti Teknologi MARA (UiTM). <http://terminalib.uitm.edu.my/77964.pdf>
institution Universiti Teknologi Mara
building Tun Abdul Razak Library
collection Institutional Repository
continent Asia
country Malaysia
content_provider Universiti Teknologi Mara
content_source UiTM Institutional Repository
url_provider http://ir.uitm.edu.my/
language English
topic Physical properties
Metals
spellingShingle Physical properties
Metals
Md. Nor, Muhammad Syafiq
The aqueous environmental effects on Co-Ni-Fe coated stainless steel bolts / Muhammad Syafiq Md.Nor
description Stainless steel 304 (SS304) is one of the widely used steel fasteners in both commercial and industrial sectors. However, stainless steel is susceptible to failure in a harsh corrosive environment despite its good corrosion resistance. Nowadays, the electrodeposition process is gaining traction as a flexible method to improve surface properties using various types of alloys. In this study, Co-Ni-Fe alloy was chosen as a protective coating for SS304 bolts through electrodeposition process. The purposes of this research are to develop a better understanding on the surface properties of Co-Ni-Fe thin film deposited onto stainless steel 304 bolt and the corrosion behaviour in corrosive mediums taken from actual environments. First, the coatings were synthesised with deposition time of 15, 30, and 45 minutes and current density of 28, 35, and 42 mA/cm2 whereas the other plating parameters were kept constant. The samples were characterised using scanning electron microscope (surface morphology and elemental composition), 3D surface metrology system (roughness and thickness), and hardness testing machine (microhardness). In most cases, there was a correlation between the trends of surface roughness and corrosion rate. Both properties had lower values as deposition time increased. In order to select the best combination of plating parameters for environmental tests, the samples were further analysed with potentiodynamic polarisation technique using a potentiostat to obtain the corrosion rates. The optimum plating parameters were 30 minutes and 42 mA/cm2 because the corrosion rate was the lowest. More samples were produced using these optimum parameters for the environmental immersion test, which consisted of river water, tap water and seawater. River water was the most aggressive environment because the samples lost the highest weight followed by seawater and tap water during the weight loss analysis. Electrochemical impedance spectroscopy (EIS) results indicated that the impedance |Z| value varied as immersion period increase. River and tap water had an increasing |Z| value whereas seawater had a decreasing |Z| value over times. In terms of electrochemical aspects, river water caused the highest corrosion rate whereas the weight loss test showed that seawater caused the highest corrosion rate. It did not had direct relationship with weight loss trend. Based on these environmental tests, the corrosion resistance of Co-Ni-Fe coating is the highest in tap water, followed by river water and seawater.
format Thesis
author Md. Nor, Muhammad Syafiq
author_facet Md. Nor, Muhammad Syafiq
author_sort Md. Nor, Muhammad Syafiq
title The aqueous environmental effects on Co-Ni-Fe coated stainless steel bolts / Muhammad Syafiq Md.Nor
title_short The aqueous environmental effects on Co-Ni-Fe coated stainless steel bolts / Muhammad Syafiq Md.Nor
title_full The aqueous environmental effects on Co-Ni-Fe coated stainless steel bolts / Muhammad Syafiq Md.Nor
title_fullStr The aqueous environmental effects on Co-Ni-Fe coated stainless steel bolts / Muhammad Syafiq Md.Nor
title_full_unstemmed The aqueous environmental effects on Co-Ni-Fe coated stainless steel bolts / Muhammad Syafiq Md.Nor
title_sort aqueous environmental effects on co-ni-fe coated stainless steel bolts / muhammad syafiq md.nor
publishDate 2022
url https://ir.uitm.edu.my/id/eprint/77964/1/77964.pdf
https://ir.uitm.edu.my/id/eprint/77964/
_version_ 1768011679435587584
score 13.222552

Similar Items