Study of selected bamboo species on the enhancement of recycled paper properties / Nur Musfirah Suhaimi
Recycled paper is already used as a replacement for pulp and paper raw material as away to minimize emissions of greenhouse gases that contribute to climate change. Homification of recycled paper has decreased its conformability and inter fiber bonding capacity. The effect of the bamboo fiber (Aur,...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2022
|
| Subjects: | |
| Online Access: | https://ir.uitm.edu.my/id/eprint/77677/1/77677.pdf https://ir.uitm.edu.my/id/eprint/77677/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Recycled paper is already used as a replacement for pulp and paper raw material as away to minimize emissions of greenhouse gases that contribute to climate change. Homification of recycled paper has decreased its conformability and inter fiber bonding capacity. The effect of the bamboo fiber (Aur, Semantan, and Beting) to enhance the strength of recycled fiber was investigated Technical Association of Pulp and Paper Industry (TAPPI) standard methods were used as guidelines for this study. The bamboo was pulped using soda anthraquinone (AQ) pulping with the pulping condition of 20 %NaOH, 170 °C pulping temperature, 1:6 bamboos to liquor ratio, 0.1 % AQ, 90 min time to reach pulping temperature, and 90 min time at pulping temperature. The bamboo at ages 1,3 and 5 we used in this study and age 1 showed the highest pulping yield (41.0%to 51.7%) thus was chosen to undergo the beating process of 0, 1000, 2000, 4000, and8000 revolutions, and beating revolution 4000 gave the optimum result for the paper mechanical properties [Aur (tensile index 55.40 Nm/g, bursting index 4.75 kPa.m2/g, tearing index 9.76 mN.m2/g and folding endurance 285 double folds), Beting (tensile index 66.49 Nm/g, bursting index 5.82 kPa.m2/g, tearing index 16.26 mN.m2/g and folding endurance 709 double folds) and Semantan (tensile index was 50.65 Nm/g, bursting index was 4.74 kPa.m2/g, tearing index was 16.63 mN.m2/g and folding endurance was 222 double folds)]. Then bamboo pulp was then combined with recycled paper pulp. The outcomes showed that when the percentage of beaten bamboo fiber in the recycled pulp increased, the mechanical properties of recycled paper were also increased. Thus, Malaysian bamboo is very promising for improving and enhancing the characteristics of recycled paper. As a result, bamboo is a viable alternative to the already imported virgin softwood pulps. |
|---|