Degradation of azo dyes in aqueous solution by using fenton process and tio2 as a catalyst / Alya Nadhira Nasron
Releasing of dyes to the environment that caused major pollutant in wastewater usually comes from textile industries. Most of dye used was azo dyes. Degradation of azo dyes by using Fenton process and TiO2 catalyst was ascertained. The type azo dyes that have been used in this study was Congo red. T...
Saved in:
| Main Author: | |
|---|---|
| Format: | Student Project |
| Language: | English |
| Published: |
Faculty of Applied Sciences
2017
|
| Subjects: | |
| Online Access: | http://ir.uitm.edu.my/id/eprint/26875/1/PPb_ALYA%20NADHIRA%20NASRON%20AS%20N%2017_5.pdf http://ir.uitm.edu.my/id/eprint/26875/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Releasing of dyes to the environment that caused major pollutant in wastewater usually comes from textile industries. Most of dye used was azo dyes. Degradation of azo dyes by using Fenton process and TiO2 catalyst was ascertained. The type azo dyes that have been used in this study was Congo red. The sample was tested under UV light and the reaction time in this experiment was conducted for 90 minutes with 15 minutes time interval. The rate degradation of dye was detected by UV-Vis spectrophotometry. The effect of several parameters in this degradation process such as the concentration of FeSO4.7H2O as a catalyst in Fenton process, the concentration of hydrogen peroxides (H2O2), mass of TiO2 and value of pH of the dye solution were investigated. The initial Congo red concentration for both Fenton process and TiO2 catalyst in this experiment was 5 ppm. The ratio of Fe2+ /H2O2 is found equal to 1 :4 to give the best result for the degradation rate. The optimum condition of Fenton process was 0.05 M Fe2+ ions and 0.2 M H2O2 and results 99.92% degradation rate. For TiO2, 0.1999 g of TiO2 dose was the optimum condition in this process which results 99.32% degradation rate after 90 minutes reaction time. The best operation condition for both Fenton reagent and TiO2 catalyst was obtained at pH 3. The results showed that the degradation of Congo red was effective in Fenton process compared to TiO2. |
|---|