Study on C02 Corrosion in Oil Producing Well
The purpose of this project is to study the C02 corrosion in oil production wells and the focus of the study will be on the tubing component of the production string. The main objectives of the project are; a) To study the material used in a well production string. b) To determine the average C02...
Saved in:
| Main Author: | |
|---|---|
| Format: | Final Year Project |
| Language: | English |
| Published: |
Universiti Teknologi PETRONAS
2009
|
| Subjects: | |
| Online Access: | http://utpedia.utp.edu.my/9147/1/2009%20-%20Study%20on%20CO2%20Corrosion%20in%20oil%20Producing%20Well.pdf http://utpedia.utp.edu.my/9147/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | The purpose of this project is to study the C02 corrosion in oil production wells and
the focus of the study will be on the tubing component of the production string. The
main objectives of the project are; a) To study the material used in a well production
string. b) To determine the average C02 corrosion rate of a typical well production
string. As for the problem statement of this project, in oil and gas industry, C02
corrosion has been a recognized problem in production and transportation facilities
for many years e.g. in the tubing string of an oil producing well. The corroded tubing
will cause leakage and tubing failure hence, disrupt oil production. The scopes of
study for this project consist of identifying the rate of C02 corrosion during the
production life time of the tubing string and determine the factors leading to the C02
corrosion. In order to provide a reliable prediction on the behavior of C02 corrosion
on tubing steel, the project's methodology used Weight Loss Method using
Autoclave Machine and Linear Polarization Resistance Method (LPR) to simulate
the actual environment in the tubing during the oil production and analyze the C02
corrosion rate. The laboratory experiments are conducted on API L 80 type steel.
The Weighted Loss Method is conducted in stagnant condition using 3 wt% NaCl
over a series of parameters which includes pressure = l 0 bar, 40 bar and 60 bar,
pH=5 and temperature at 25 DC. The LPR method is conducted in flowing solution
using 3 wt% NaCl over a series of parameters which includes temperature = 25 OC,
40 T and 60 T, pH = 5 and pressure at 1 atm. All data were collected and analyzed
using Weighted Loss Method, LPR, SEM, OM and Hardness (Vicker) Test to
determine the C02 corrosion rate and the effects on the L 80 steel. As for the
findings, the average C02 corrosion rates in API L 80 steel yield from the laboratory
test ranges from 1.3 mm/yr to 4. 7 mm/yr. |
|---|