Preparation and properties characterization of P2O5-KNO3-K2O glass
A series of glass based on 50P2O5-xKNO3-(50-x) K2O system where 0 < x £ 50 mol % has successfully been prepared using melt-quenched technique. The glass crystallinity has been confirmed using X-Ray Diffraction (XRD) analysis while the microhardness is measured using Vickers indenter. It is found...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | en |
| Published: |
2005
|
| Subjects: | |
| Online Access: | http://eprints.utm.my/4181/1/MohdHelmyHashimMFS2005.pdf http://eprints.utm.my/4181/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1845471060668973056 |
|---|---|
| author | Hashim, Mohd. Helmy |
| author_facet | Hashim, Mohd. Helmy |
| author_sort | Hashim, Mohd. Helmy |
| building | UTM Library |
| collection | Institutional Repository |
| content_provider | Universiti Teknologi Malaysia |
| content_source | UTM Institutional Repository |
| continent | Asia |
| country | Malaysia |
| description | A series of glass based on 50P2O5-xKNO3-(50-x) K2O system where 0 < x £ 50 mol % has successfully been prepared using melt-quenched technique. The glass crystallinity has been confirmed using X-Ray Diffraction (XRD) analysis while the microhardness is measured using Vickers indenter. It is found that the microhardness is in the range of 146 Hv to178 Hv as the mol % of KNO3 content increases. The glass density, which is measured using the digital balance, is found to be in the range of 2.3820 gcm-3 to 2.4232 gcm-3 as the mol % of KNO3 content increases. The molecular bond structures and the characteristic of H-OH molecular vibrations in the glass are investigated using Infrared absorption spectrometer in the range of 370 cm-1 to 3800 cm-1. It has been found that the nitrogen incorporated into the glass network by replacing the bridging oxygen. It is also found out that the increase in the mol % of KNO3 content will cause the corrosion rate of the glass in pH 1, pH 3, pH 5 and pH 7 solutions to fall from 5.83 x 10-3 gcm-2min-1 to 0.25 x 10-3 gcm-2min-1. All of the solutions experience the increase in pH value after the 20 minutes corrosion test. |
| format | Thesis |
| id | my.utm.eprints-4181 |
| institution | Universiti Teknologi Malaysia |
| language | en |
| publishDate | 2005 |
| record_format | eprints |
| spelling | my.utm.eprints-41812018-01-15T07:32:09Z http://eprints.utm.my/4181/ Preparation and properties characterization of P2O5-KNO3-K2O glass Hashim, Mohd. Helmy QC Physics A series of glass based on 50P2O5-xKNO3-(50-x) K2O system where 0 < x £ 50 mol % has successfully been prepared using melt-quenched technique. The glass crystallinity has been confirmed using X-Ray Diffraction (XRD) analysis while the microhardness is measured using Vickers indenter. It is found that the microhardness is in the range of 146 Hv to178 Hv as the mol % of KNO3 content increases. The glass density, which is measured using the digital balance, is found to be in the range of 2.3820 gcm-3 to 2.4232 gcm-3 as the mol % of KNO3 content increases. The molecular bond structures and the characteristic of H-OH molecular vibrations in the glass are investigated using Infrared absorption spectrometer in the range of 370 cm-1 to 3800 cm-1. It has been found that the nitrogen incorporated into the glass network by replacing the bridging oxygen. It is also found out that the increase in the mol % of KNO3 content will cause the corrosion rate of the glass in pH 1, pH 3, pH 5 and pH 7 solutions to fall from 5.83 x 10-3 gcm-2min-1 to 0.25 x 10-3 gcm-2min-1. All of the solutions experience the increase in pH value after the 20 minutes corrosion test. 2005-10 Thesis NonPeerReviewed application/pdf en http://eprints.utm.my/4181/1/MohdHelmyHashimMFS2005.pdf Hashim, Mohd. Helmy (2005) Preparation and properties characterization of P2O5-KNO3-K2O glass. Masters thesis, Universiti Teknologi Malaysia, Faculty of Science. |
| spellingShingle | QC Physics Hashim, Mohd. Helmy Preparation and properties characterization of P2O5-KNO3-K2O glass |
| title | Preparation and properties characterization of P2O5-KNO3-K2O glass |
| title_full | Preparation and properties characterization of P2O5-KNO3-K2O glass |
| title_fullStr | Preparation and properties characterization of P2O5-KNO3-K2O glass |
| title_full_unstemmed | Preparation and properties characterization of P2O5-KNO3-K2O glass |
| title_short | Preparation and properties characterization of P2O5-KNO3-K2O glass |
| title_sort | preparation and properties characterization of p2o5-kno3-k2o glass |
| topic | QC Physics |
| url | http://eprints.utm.my/4181/1/MohdHelmyHashimMFS2005.pdf http://eprints.utm.my/4181/ |
| url_provider | http://eprints.utm.my/ |