High temperature cyclic oxidation of Ti-Al based intermetallic in static laboratory air
The objective of this study is to investigate the oxidation behavior of binary ?-TiAl based intermetallic; with composition (at%) of 45A, 48Al and 50Al, and ternary alloys of Ti-48Al containing 2Cr and 4Cr. Thermal cyclic oxidation was conducted discontinuously at temperatures of 7000C and 9000...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | en |
| Published: |
2007
|
| Subjects: | |
| Online Access: | http://eprints.utm.my/10030/2/AstutyAmrin2007_HighTemperatureCyclicOxidationTi.pdf http://eprints.utm.my/10030/ http://dms.library.utm.my:8080/vital/access/manager/Repository/vital:103073 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1845472290046738432 |
|---|---|
| author | Amrin, Astuty Hamzah, Esah Mohd. Badri, Nurfashahidayu Hamzah, Hafida |
| author_facet | Amrin, Astuty Hamzah, Esah Mohd. Badri, Nurfashahidayu Hamzah, Hafida |
| author_sort | Amrin, Astuty |
| building | UTM Library |
| collection | Institutional Repository |
| content_provider | Universiti Teknologi Malaysia |
| content_source | UTM Institutional Repository |
| continent | Asia |
| country | Malaysia |
| description | The objective of this study is to investigate
the oxidation behavior of binary ?-TiAl based
intermetallic; with composition (at%) of 45A, 48Al and
50Al, and ternary alloys of Ti-48Al containing 2Cr and
4Cr. Thermal cyclic oxidation was conducted
discontinuously at temperatures of 7000C and 9000C in
static laboratory air. Optical microscopy, Scanning
Electron Microscopy (FESEM), Energy Dispersive Xray
Analysis (EDX) and X-ray diffraction (XRD)
techniques were employed for the analysis. SEM
examination of cross-sectional samples using secondary
electron and line-scan analysis after exposure at 7000C
showed that non-adherent oxides scales formed due to
the spallation caused by cyclic condition. While,
exposure at 9000C, only binary alloys exhibited
breakaway oxidation while the oxides scale formed on
the ternary alloys were well-adhered on the substrate
alloy. Overall, exposure at 9000C resulted in thicker and
harder oxide scales and addition of Cr believed to
improve oxidation resistance of Ti-Al based
intermetallics at higher temperature |
| format | Conference or Workshop Item |
| id | my.utm.eprints-10030 |
| institution | Universiti Teknologi Malaysia |
| language | en |
| publishDate | 2007 |
| record_format | eprints |
| spelling | my.utm.eprints-100302020-03-17T08:03:48Z http://eprints.utm.my/10030/ High temperature cyclic oxidation of Ti-Al based intermetallic in static laboratory air Amrin, Astuty Hamzah, Esah Mohd. Badri, Nurfashahidayu Hamzah, Hafida TJ Mechanical engineering and machinery The objective of this study is to investigate the oxidation behavior of binary ?-TiAl based intermetallic; with composition (at%) of 45A, 48Al and 50Al, and ternary alloys of Ti-48Al containing 2Cr and 4Cr. Thermal cyclic oxidation was conducted discontinuously at temperatures of 7000C and 9000C in static laboratory air. Optical microscopy, Scanning Electron Microscopy (FESEM), Energy Dispersive Xray Analysis (EDX) and X-ray diffraction (XRD) techniques were employed for the analysis. SEM examination of cross-sectional samples using secondary electron and line-scan analysis after exposure at 7000C showed that non-adherent oxides scales formed due to the spallation caused by cyclic condition. While, exposure at 9000C, only binary alloys exhibited breakaway oxidation while the oxides scale formed on the ternary alloys were well-adhered on the substrate alloy. Overall, exposure at 9000C resulted in thicker and harder oxide scales and addition of Cr believed to improve oxidation resistance of Ti-Al based intermetallics at higher temperature 2007-12-26 Conference or Workshop Item NonPeerReviewed application/pdf en http://eprints.utm.my/10030/2/AstutyAmrin2007_HighTemperatureCyclicOxidationTi.pdf Amrin, Astuty and Hamzah, Esah and Mohd. Badri, Nurfashahidayu and Hamzah, Hafida (2007) High temperature cyclic oxidation of Ti-Al based intermetallic in static laboratory air. In: 2nd National Metallurgical Conference 2007, 26-27th November 2007, The Puteri Pan Pacific, Johor Bahru. http://dms.library.utm.my:8080/vital/access/manager/Repository/vital:103073 |
| spellingShingle | TJ Mechanical engineering and machinery Amrin, Astuty Hamzah, Esah Mohd. Badri, Nurfashahidayu Hamzah, Hafida High temperature cyclic oxidation of Ti-Al based intermetallic in static laboratory air |
| title | High temperature cyclic oxidation of Ti-Al based intermetallic in static laboratory air |
| title_full | High temperature cyclic oxidation of Ti-Al based intermetallic in static laboratory air |
| title_fullStr | High temperature cyclic oxidation of Ti-Al based intermetallic in static laboratory air |
| title_full_unstemmed | High temperature cyclic oxidation of Ti-Al based intermetallic in static laboratory air |
| title_short | High temperature cyclic oxidation of Ti-Al based intermetallic in static laboratory air |
| title_sort | high temperature cyclic oxidation of ti-al based intermetallic in static laboratory air |
| topic | TJ Mechanical engineering and machinery |
| url | http://eprints.utm.my/10030/2/AstutyAmrin2007_HighTemperatureCyclicOxidationTi.pdf http://eprints.utm.my/10030/ http://dms.library.utm.my:8080/vital/access/manager/Repository/vital:103073 |
| url_provider | http://eprints.utm.my/ |