Observation of the fatigue crack propagation rate of an aluminum alloy specimen under fatigue spectrum loadings
This paper presents an assessment on fatigue crack propagation (FCG) behavior and fractography observation for an aluminum alloy that was exposed under spectrum loadings. The FCG test has three types of cyclic loadings, namely, constant-amplitude loading (CAL) as well as high-to-low and low-to-high...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | en |
| Published: |
2012
|
| Subjects: | |
| Online Access: | http://eprints.utem.edu.my/id/eprint/8523/1/MP110376_Zakaria.pdf http://eprints.utem.edu.my/id/eprint/8523/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1832716307197329408 |
|---|---|
| author | Abdullah, Shahrum Zakaria, Kamarul Ariffin Ghazali, Mariyam Jameelah |
| author_facet | Abdullah, Shahrum Zakaria, Kamarul Ariffin Ghazali, Mariyam Jameelah |
| author_sort | Abdullah, Shahrum |
| building | UTEM Library |
| collection | Institutional Repository |
| content_provider | Universiti Teknikal Malaysia Melaka |
| content_source | UTEM Institutional Repository |
| continent | Asia |
| country | Malaysia |
| description | This paper presents an assessment on fatigue crack propagation (FCG) behavior and fractography observation for an aluminum alloy that was exposed under spectrum loadings. The FCG test has three types of cyclic loadings, namely, constant-amplitude loading (CAL) as well as high-to-low and low-to-high sequence loadings. All three have been performed on the Al6061-T6 specimens. The tests were performed using a 100 kN servo-hydraulic fatigue testing machine following an ASTM E647 standard. The results show that fatigue crack propagation and its fractography were influenced by the load interaction and the sequence, which affect the fracture behavior of aluminum alloys. The fracture surface exhibited irregular local striation spacings under the spectrum loading. Moreover, the micrographs show increased plasticity throughout the crack propagation compared to CAL. |
| format | Article |
| id | my.utem.eprints-8523 |
| institution | Universiti Teknikal Malaysia Melaka |
| language | en |
| publishDate | 2012 |
| record_format | eprints |
| spelling | my.utem.eprints-85232015-05-28T03:57:14Z http://eprints.utem.edu.my/id/eprint/8523/ Observation of the fatigue crack propagation rate of an aluminum alloy specimen under fatigue spectrum loadings Abdullah, Shahrum Zakaria, Kamarul Ariffin Ghazali, Mariyam Jameelah TJ Mechanical engineering and machinery This paper presents an assessment on fatigue crack propagation (FCG) behavior and fractography observation for an aluminum alloy that was exposed under spectrum loadings. The FCG test has three types of cyclic loadings, namely, constant-amplitude loading (CAL) as well as high-to-low and low-to-high sequence loadings. All three have been performed on the Al6061-T6 specimens. The tests were performed using a 100 kN servo-hydraulic fatigue testing machine following an ASTM E647 standard. The results show that fatigue crack propagation and its fractography were influenced by the load interaction and the sequence, which affect the fracture behavior of aluminum alloys. The fracture surface exhibited irregular local striation spacings under the spectrum loading. Moreover, the micrographs show increased plasticity throughout the crack propagation compared to CAL. 2012 Article PeerReviewed application/pdf en http://eprints.utem.edu.my/id/eprint/8523/1/MP110376_Zakaria.pdf Abdullah, Shahrum and Zakaria, Kamarul Ariffin and Ghazali, Mariyam Jameelah (2012) Observation of the fatigue crack propagation rate of an aluminum alloy specimen under fatigue spectrum loadings. Materials Testing, 54 (10). pp. 663-673. ISSN ISSN 0025-5300 |
| spellingShingle | TJ Mechanical engineering and machinery Abdullah, Shahrum Zakaria, Kamarul Ariffin Ghazali, Mariyam Jameelah Observation of the fatigue crack propagation rate of an aluminum alloy specimen under fatigue spectrum loadings |
| title | Observation of the fatigue crack propagation rate of an aluminum alloy specimen under fatigue spectrum loadings |
| title_full | Observation of the fatigue crack propagation rate of an aluminum alloy specimen under fatigue spectrum loadings |
| title_fullStr | Observation of the fatigue crack propagation rate of an aluminum alloy specimen under fatigue spectrum loadings |
| title_full_unstemmed | Observation of the fatigue crack propagation rate of an aluminum alloy specimen under fatigue spectrum loadings |
| title_short | Observation of the fatigue crack propagation rate of an aluminum alloy specimen under fatigue spectrum loadings |
| title_sort | observation of the fatigue crack propagation rate of an aluminum alloy specimen under fatigue spectrum loadings |
| topic | TJ Mechanical engineering and machinery |
| url | http://eprints.utem.edu.my/id/eprint/8523/1/MP110376_Zakaria.pdf http://eprints.utem.edu.my/id/eprint/8523/ |
| url_provider | http://eprints.utem.edu.my/ |