Mechanical performance and corrosion behaviour of diffusion-bonded A5083 aluminium and A36 mild steel with gallium interlayer
This article investigated the mechanical performance and corrosion behaviour of a diffusion-bonded A5083 aluminium/A36 mild steel dissimilar joint with a Gallium (Ga) interlayer. The bonding parameters were the bonding temperature (525 and 550 °C), holding time (60 and 120 min) and surface roughness...
Saved in:
| Main Authors: | , , , , , , , |
|---|---|
| Format: | Article |
| Published: |
Multidisciplinary Digital Publishing Institute
2022
|
| Online Access: | http://psasir.upm.edu.my/id/eprint/102155/ https://www.mdpi.com/1996-1944/15/18/6331 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | This article investigated the mechanical performance and corrosion behaviour of a diffusion-bonded A5083 aluminium/A36 mild steel dissimilar joint with a Gallium (Ga) interlayer. The bonding parameters were the bonding temperature (525 and 550 °C), holding time (60 and 120 min) and surface roughness (800 and 1200 grit). Property characterisation was achieved using Scanning Electron Microscopy (SEM), Energy Dispersive X-ray (EDX) analysis, Vickers microhardness tester, Izod impact tester and potentiodynamic polarisation testing. The results revealed that the significance of the bonding parameters was in the order bonding temperature > surface roughness > holding time. Increasing the bonding temperature resulted in an increase in the impact strength and a corresponding reduction in the corrosion rate and microhardness. However, increasing the grit size decreased the microhardness and a corresponding increase in the impact strength and corrosion rate. The impact strength and corrosion rate decreased with the increasing holding time while the microhardness followed a reverse trend. It was also discovered that incorporating the Ga interlayer resulted in a 67.9% improvement in the degradation rate. |
|---|