The transport critical current of AG-Sheathed (T1,Cr) Sr2CaCu2O7 superconductor tapes
The measurement of the transport critical current of T1-1212 superconductor tapes at three different annealing temperature and time were completed and recorded using the 1uV/cm criteria. The superconductor tapes labeled asM1, M10 and M11 were annealed at temperature of 890C for 30 minutes, 800C for...
Saved in:
| Main Author: | |
|---|---|
| Format: | text::Thesis |
| Language: | en |
| Published: |
2023
|
| Subjects: | |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1848452265726181376 |
|---|---|
| author | Nor Salwa Bt. Hamdan |
| author_facet | Nor Salwa Bt. Hamdan |
| author_sort | Nor Salwa Bt. Hamdan |
| building | UNITEN Library |
| collection | Institutional Repository |
| content_provider | Universiti Tenaga Nasional |
| content_source | UNITEN Institutional Repository |
| continent | Asia |
| country | Malaysia |
| description | The measurement of the transport critical current of T1-1212 superconductor tapes at three different annealing temperature and time were completed and recorded using the 1uV/cm criteria. The superconductor tapes labeled asM1, M10 and M11 were annealed at temperature of 890C for 30 minutes, 800C for 30 minutes and 800C for 1 hour respectively. The readings for the V-1 characteristics were obtained through the implementation of the standard four-point probe attached to the superconductor tapes and immersed in the boiling temperature of liquid nitrogen. The values of the V-1 characteristics were converted to uV/cm values by dividing the voltage values with the length of two voltage probes. From 1uV/cm criteria for the three tapes, we found that M10 has the highest value of critical current, I and no critical current was obtained sample M1. |
| format | Resource Types::text::Thesis |
| id | my.uniten.dspace-20880 |
| institution | Universiti Tenaga Nasional |
| language | en |
| publishDate | 2023 |
| record_format | dspace |
| spelling | my.uniten.dspace-208802025-10-28T12:11:10Z The transport critical current of AG-Sheathed (T1,Cr) Sr2CaCu2O7 superconductor tapes Nor Salwa Bt. Hamdan Superconductivity The measurement of the transport critical current of T1-1212 superconductor tapes at three different annealing temperature and time were completed and recorded using the 1uV/cm criteria. The superconductor tapes labeled asM1, M10 and M11 were annealed at temperature of 890C for 30 minutes, 800C for 30 minutes and 800C for 1 hour respectively. The readings for the V-1 characteristics were obtained through the implementation of the standard four-point probe attached to the superconductor tapes and immersed in the boiling temperature of liquid nitrogen. The values of the V-1 characteristics were converted to uV/cm values by dividing the voltage values with the length of two voltage probes. From 1uV/cm criteria for the three tapes, we found that M10 has the highest value of critical current, I and no critical current was obtained sample M1. 2023-05-03T15:30:22Z 2023-05-03T15:30:22Z 2001 Resource Types::text::Thesis https://irepository.uniten.edu.my/handle/123456789/20880 en application/pdf |
| spellingShingle | Superconductivity Nor Salwa Bt. Hamdan The transport critical current of AG-Sheathed (T1,Cr) Sr2CaCu2O7 superconductor tapes |
| title | The transport critical current of AG-Sheathed (T1,Cr) Sr2CaCu2O7 superconductor tapes |
| title_full | The transport critical current of AG-Sheathed (T1,Cr) Sr2CaCu2O7 superconductor tapes |
| title_fullStr | The transport critical current of AG-Sheathed (T1,Cr) Sr2CaCu2O7 superconductor tapes |
| title_full_unstemmed | The transport critical current of AG-Sheathed (T1,Cr) Sr2CaCu2O7 superconductor tapes |
| title_short | The transport critical current of AG-Sheathed (T1,Cr) Sr2CaCu2O7 superconductor tapes |
| title_sort | transport critical current of ag-sheathed (t1,cr) sr2cacu2o7 superconductor tapes |
| topic | Superconductivity |
| url_provider | http://dspace.uniten.edu.my/ |