Formation of nano-crystalline phase in hydrogenated amorphous silicon thin film by plasma focus ion beam irradiation
A 3.3 kJ Mather type dense plasma focus device is used to generate a pulsed argon ion beam of 100 KeV in this work. Hydrogenated amorphous silicon (a-Si:H) film prepared by plasma enhanced chemical vapor deposition (PECVD) on c-Si substrate was irradiated with the argon ion beam produced by this den...
Saved in:
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Published: |
2012
|
| Subjects: | |
| Online Access: | http://eprints.um.edu.my/7354/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | A 3.3 kJ Mather type dense plasma focus device is used to generate a pulsed argon ion beam of 100 KeV in this work. Hydrogenated amorphous silicon (a-Si:H) film prepared by plasma enhanced chemical vapor deposition (PECVD) on c-Si substrate was irradiated with the argon ion beam produced by this dense plasma focus device. The effects of exposure to a single, 5 and 10 shots of dense plasma focus argon ion beam irradiation on the surface morphology, crystallinity and chemical bonding properties of the a-Si:H films were studied using Field Emission Scanning Electron Microscope (FESEM), X-ray Diffraction (XRD), Raman scattering and Fourier Transform Infrared (FTIR) spectroscopy, respectively. Formation of nano-crystalline silicon phase along with increase in structural order and hydrogen content in the film structure has been observed when the a-Si:H film was irradiated with a single shot of dense plasma focus argon ion beam. Exposure to 5 and 10 shots of the dense plasma focus argon ion beam irradiation reduced the hydrogen content resulting in a decrease in crystallinity and structural order in the film structure. |
|---|