Study of fatigue crack propagation (FCP) of polymethylmethacrylate (PMMA) at a different R ratio / Hashim Abu Hassan
The exact nature of the mechanisms involved in the fatigue failure of polymeric material is by no means well understood . Eventhough a great amount of research effort has been focus on the study of various aspects of the phenomena with component failure under repeated loading conditions, a general c...
Saved in:
| Main Author: | |
|---|---|
| Format: | Student Project |
| Language: | en |
| Published: |
1991
|
| Subjects: | |
| Online Access: | https://ir.uitm.edu.my/id/eprint/73228/1/73228.pdf https://ir.uitm.edu.my/id/eprint/73228/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1833075373346127872 |
|---|---|
| author | Abu Hassan, Hashim |
| author_facet | Abu Hassan, Hashim |
| author_sort | Abu Hassan, Hashim |
| building | Tun Abdul Razak Library |
| collection | Institutional Repository |
| content_provider | Universiti Teknologi Mara |
| content_source | UiTM Institutional Repository |
| continent | Asia |
| country | Malaysia |
| description | The exact nature of the mechanisms involved in the fatigue failure of polymeric material is by no means well understood . Eventhough a great amount of research effort has been focus on the study of various aspects of the phenomena with component failure under repeated loading conditions, a general criterion for analysis of such failures has not yet established. The aim of this paper is to examine the empirical evidence on the pattern of crack propagation in Polymethylmethacrylate in the light of linear elastic fracture mechanics concepts and to demonstrate that a particular criterion related to the stress intensity factor, K , with the different values of Rratio. Compact type specimens are used with dynamic load control Instron Machine Model 8032. Surface crack propagations are observed using traveling microscope in an increamental of 0.1 mm. Fatigue crack propagation resistance shown improved a s the Rratio decrease.Another parameter, Kmean arises where it should considered and others paper result are included to know the effect. |
| format | Student Project |
| id | my.uitm.ir-73228 |
| institution | Universiti Teknologi Mara |
| language | en |
| publishDate | 1991 |
| record_format | eprints |
| spelling | my.uitm.ir-732282023-03-27T12:20:47Z https://ir.uitm.edu.my/id/eprint/73228/ Study of fatigue crack propagation (FCP) of polymethylmethacrylate (PMMA) at a different R ratio / Hashim Abu Hassan Abu Hassan, Hashim Mechanics of engineering. Applied mechanics Surface effects and tests The exact nature of the mechanisms involved in the fatigue failure of polymeric material is by no means well understood . Eventhough a great amount of research effort has been focus on the study of various aspects of the phenomena with component failure under repeated loading conditions, a general criterion for analysis of such failures has not yet established. The aim of this paper is to examine the empirical evidence on the pattern of crack propagation in Polymethylmethacrylate in the light of linear elastic fracture mechanics concepts and to demonstrate that a particular criterion related to the stress intensity factor, K , with the different values of Rratio. Compact type specimens are used with dynamic load control Instron Machine Model 8032. Surface crack propagations are observed using traveling microscope in an increamental of 0.1 mm. Fatigue crack propagation resistance shown improved a s the Rratio decrease.Another parameter, Kmean arises where it should considered and others paper result are included to know the effect. 1991 Student Project NonPeerReviewed text en https://ir.uitm.edu.my/id/eprint/73228/1/73228.pdf Study of fatigue crack propagation (FCP) of polymethylmethacrylate (PMMA) at a different R ratio / Hashim Abu Hassan. (1991) [Student Project] (Unpublished) |
| spellingShingle | Mechanics of engineering. Applied mechanics Surface effects and tests Abu Hassan, Hashim Study of fatigue crack propagation (FCP) of polymethylmethacrylate (PMMA) at a different R ratio / Hashim Abu Hassan |
| title | Study of fatigue crack propagation (FCP) of polymethylmethacrylate (PMMA) at a different R ratio / Hashim Abu Hassan |
| title_full | Study of fatigue crack propagation (FCP) of polymethylmethacrylate (PMMA) at a different R ratio / Hashim Abu Hassan |
| title_fullStr | Study of fatigue crack propagation (FCP) of polymethylmethacrylate (PMMA) at a different R ratio / Hashim Abu Hassan |
| title_full_unstemmed | Study of fatigue crack propagation (FCP) of polymethylmethacrylate (PMMA) at a different R ratio / Hashim Abu Hassan |
| title_short | Study of fatigue crack propagation (FCP) of polymethylmethacrylate (PMMA) at a different R ratio / Hashim Abu Hassan |
| title_sort | study of fatigue crack propagation (fcp) of polymethylmethacrylate (pmma) at a different r ratio / hashim abu hassan |
| topic | Mechanics of engineering. Applied mechanics Surface effects and tests |
| url | https://ir.uitm.edu.my/id/eprint/73228/1/73228.pdf https://ir.uitm.edu.my/id/eprint/73228/ |
| url_provider | http://ir.uitm.edu.my/ |