The durability of HoBa2Cu3O7-δ and HoBa2Cu3O7-δ (with elemental substitution- Sr at Ba site of the ceramics with the hot spot phenomena) / Mohd Farouk Afizal Ismail.
A hot spot, which is local area glowing orange appear in HoBa2Cu3O7-δ ceramics the certain voltage is applied to the rod at room temperature. The durability of the rod during a sustained presence of the hot is improved upon substitution of Sr at Ba site. In this experiment, the HoBa2Cu3O7-δ ceramics...
Saved in:
| Main Author: | |
|---|---|
| Format: | Student Project |
| Language: | en |
| Published: |
2007
|
| Subjects: | |
| Online Access: | https://ir.uitm.edu.my/id/eprint/45224/1/45224.pdf https://ir.uitm.edu.my/id/eprint/45224/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | A hot spot, which is local area glowing orange appear in HoBa2Cu3O7-δ ceramics the certain voltage is applied to the rod at room temperature. The durability of the rod during a sustained presence of the hot is improved upon substitution of Sr at Ba site. In this experiment, the HoBa2Cu3O7-δ ceramics were prepared using conventional solid-state reaction. The experiment was done using three different samples; HoBa2Cu3O7-δ without any substitution, HoBa2Cu3O7-δ with 0.3 mol% substitution and 0.5 mol% substitution of Sr at Ba site. The samples were cut into rod shape of dimension (0.65 x 0.65 x 12) mm. All the samples were tested for its current-voltage characteristics using the four-point-probe method. The voltages of hot spot appearance were determined. The durability of rod was determined by the time of appearance of hot spot. The results showed different durability for different samples. There are also some differences in power consumptions of the rod due to the Sr substitution content. |
|---|