Strenthening of alumunium with addition of nano-silicon carbide by using powder metallurgy method / Rizal Mohamed Noor, Khairul Fauzi Karim and Kamrol Amri Mohamed.
This study focuses on nano silicon carbide particulate-reinforced metal-matrix composites processing route using two different powder metallurgy techniques; cold press-sintered and hot press-vacuum. Two kinds of SiC particulates (SiCp), whose diameters 60 pm and 50-200 nm were separately incorporate...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Research Reports |
| Language: | en |
| Published: |
2006
|
| Subjects: | |
| Online Access: | https://ir.uitm.edu.my/id/eprint/42336/1/42336.pdf https://ir.uitm.edu.my/id/eprint/42336/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | This study focuses on nano silicon carbide particulate-reinforced metal-matrix composites processing route using two different powder metallurgy techniques; cold press-sintered and hot press-vacuum. Two kinds of SiC particulates (SiCp), whose diameters 60 pm and 50-200 nm were separately incorporated into Al-lwt% SiC and Al- 3wt% SiC by mechanical milling. The microstructures of the samples were investigated by means scanning electron microscopy and correlated to their mechanical properties through hardness and three-point bending test. The experiment showed that hot press- vacuum route resulted a smaller size and amount of the pores compared to cold press- sintered, thus led to the dramatically improvement in mechanical properties which result an improvement of hardness from 105.7 Hv to 450.6 and strength from 4.7 MPa to 16.2
MPa. |
|---|