Exploring joint strength and energy absorption across various clinching configurations of steel and aluminum alloy sheets
The quality and mechanical characteristics of clinched joints using the extensible die with different dissimilar materials (steel sheets and aluminum alloy), various thicknesses, and different combinations and orientations (vertical, horizontal, and quantity) of the joints were investigated in this...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | en en |
| Published: |
Springer Nature
2025
|
| Subjects: | |
| Online Access: | http://irep.iium.edu.my/120401/7/120401_%20Exploring%20joint%20strength.pdf http://irep.iium.edu.my/120401/8/120401_%20Exploring%20joint%20strength_Scopus.pdf http://irep.iium.edu.my/120401/ https://link.springer.com/article/10.1007/s00170-025-15157-y |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | The quality and mechanical characteristics of clinched joints using the extensible die with different dissimilar materials (steel sheets and aluminum alloy), various thicknesses, and different combinations and orientations (vertical, horizontal, and quantity) of the joints were investigated in this paper. Tensile shear testing was performed to obtain the mechanical characteristics of different clinched joints with combinations of dissimilar metal sheets allowing the examination of specimens under different categories of conventional and hybrid joints. In addition, the pull-out test was considered for different clinched joints. Results showed that almost all mild steel-coated, non-coated sheets and galvanized sheets joined with aluminum sheets using clinched joints failed at the neck rejoin of the joint (neck fracture mode). Moreover, the location of the thin sheet affects the joints’ quality, whereas the results indicate that joint failures occur during forming of the joint with thin sheets located at the punch side provided that the softer material is located at the die side. In general, the location of the aluminum sheets influences the load bearing capacity which has lower load capacity than when located at the die location. Hybrid clinched joints
show that the curing time and thickness of the adhesive affect the strength of the joints, whereas long curing time causes lower strength, at the same time, thick adhesive layers show lower strength than a thin adhesive layer with less curing time. |
|---|