Hydrogen production via CO2-CH4 reforming over cobalt-supported mesoporous alumina: A kinetic evaluation
The performance of cobalt supported on mesoporous alumina (MA) under the influence of reaction temperature (923 K-1073 K) and reactant partial pressure (10 kPa-40 kPa) for CO2-CH4 reforming was executed by using a tubular fixed-bed reactor. 10%Co/MA exhibited great catalytic performance (X-CH4 = 70....
保存先:
| 主要な著者: | , , , , , |
|---|---|
| フォーマット: | 論文 |
| 出版事項: |
Elsevier Ltd
2021
|
| 主題: | |
| オンライン･アクセス: | http://eprints.utm.my/id/eprint/96608/ http://dx.doi.org/10.1016/j.ijhydene.2020.04.130 |
| タグ: |
タグ追加
タグなし, このレコードへの初めてのタグを付けませんか!
|
| 要約: | The performance of cobalt supported on mesoporous alumina (MA) under the influence of reaction temperature (923 K-1073 K) and reactant partial pressure (10 kPa-40 kPa) for CO2-CH4 reforming was executed by using a tubular fixed-bed reactor. 10%Co/MA exhibited great catalytic performance (X-CH4 = 70.9%, X-CO2 = 71.7% and D-a = 1.3%), credited to the well dispersion of Co within pore MA, strong metal-support interaction, and MA confinement ability. Based on Langmuir-Hinshelwood kinetic analysis, the dissociative adsorption of both reactants on a single Co active site was selected for this study. The lower value of activation energy (28.9 kJ mol(-1)) suggested that Co particles were finely scattered on the MA surface. Regardless of carbon types, the amount of coke accumulated on the spent 10% Co/MA within 8 h of CO2-CH4 reforming was inhibited due to fine Co distribution inside MA structure, as well as lessened with the raise of reforming temperature from 923 to 1073 K due to improvement in reverse Boudouard reaction. |
|---|