Optimization of wear and hardness of al Al–Zn–Mg–Cu alloy fabricated from recycled beverage can using response surface methodology
A novel X7475 (Al–Zn–Mg–Cu) alloy was fabricated from recycled beverage cans (RBCs). Al was recovered from RBC. Zn and Mn were sourced from spent batteries, while Cu was sourced from copper wire. The weight percent (wt%) Zn was varied at 4, 4.5 and 5. Following the fabrication of rods, samples were...