Thermoluminescence properties of optical fibers doped with RE+3 (RE=Sm, Nd) ions subjected to X-ray irradiation
This paper describes the thermoluminescence properties of RE+3(RE=Nd, Sm) doped optical fiber SiO2. The samples were exposed to 6 MV X-ray irradiation at dose ranging from 0.5 to 4 Gy at hospital Sultan Ismail, Johor Bahru, Malaysia using the LINAC accelerator. After exposure and a certain delay of...
محفوظ في:
| المؤلفون الرئيسيون: | , , |
|---|---|
| التنسيق: | Conference or Workshop Item |
| منشور في: |
2013
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | http://eprints.utm.my/id/eprint/63633/ http://dx.doi.org/10.4028/www.scientific.net/AMM.606.19 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| الملخص: | This paper describes the thermoluminescence properties of RE+3(RE=Nd, Sm) doped optical fiber SiO2. The samples were exposed to 6 MV X-ray irradiation at dose ranging from 0.5 to 4 Gy at hospital Sultan Ismail, Johor Bahru, Malaysia using the LINAC accelerator. After exposure and a certain delay of 12 h to get uniform control of thermal fading, the optical fiber TL yield was readout using a thermoluminescence (TL) reader. The optical fiber demonstrated a linear TL response versus of the absorbed dose. The linearity increases with the increasing dose while in the case of Sm-doped optical fiber, the response is comparatively smaller than Nd-doped optical fiber. Also, the glow curve of RE+3 ions doped optical fiber was compared with the undoped fibers. The results exhibit that the glow curve peaks are shifted to higher temperature due to rare-earth doping. The results indicate the TL response strongly depends on the doping type of materials. All these TL characteristics are proposing this commercial optical fiber very decisive TL material. |
|---|