Uv-visible photodegradation of methylene blue doped in poly(vinyl alcohol)(PVA) solid matrix
In this paper, The photobleaching of methylene blue (MB) doped in poly(vinyl alcohol) (PVA) matrix was investigated using an uv-visible fibre optic spectrophotometer. The absorption observed at 660nm decreases with the increasing of the exposure time. The blue color of the MB doped PVA sample turned...
保存先:
| 主要な著者: | , , , , |
|---|---|
| フォーマット: | 論文 |
| 言語: | English |
| 出版事項: |
Malaysian Solid State Science and Technology Society
2003
|
| オンライン･アクセス: | http://psasir.upm.edu.my/id/eprint/42204/1/Uv-visible%20photodegradation%20of%20methylene%20blue%20doped%20in%20poly%28vinyl%20alcohol%29%28PVA%29%20solid%20matrix.pdf http://psasir.upm.edu.my/id/eprint/42204/ http://masshp.net/journal/all%20journal/VOLUME%2011%20NO.%201,%202003/htm/Vol.%2011,%20No.1%20%282003%29%20124-%20130.htm |
| タグ: |
タグ追加
タグなし, このレコードへの初めてのタグを付けませんか!
|
| 要約: | In this paper, The photobleaching of methylene blue (MB) doped in poly(vinyl alcohol) (PVA) matrix was investigated using an uv-visible fibre optic spectrophotometer. The absorption observed at 660nm decreases with the increasing of the exposure time. The blue color of the MB doped PVA sample turned completely colorless after irradiation for 360 seconds. The optical transmission of the samples at different dye concentration was measured in the range of 450-800nm. The photobleaching mechanism in the present sample was also discussed. The experimental results shown that the material studied could be a good candidate for waveguide devices. |
|---|