Graphite whiskers derived from waste coffee grounds treated at high temperature
Graphite whiskers (GWs) are obtained from coffee grounds (CGs) treated at 2500 °C for 1 h in the presence of Ar gas at 1 atm. The majority of the GWs formed inside the CGs shell are rod-like with a conical tip with diameter and length in the range between 1 to 3 µm and 4 to 10 µm, respectively. At f...
Saved in:
| Main Authors: | , , , , , , |
|---|---|
| 格式: | Article |
| 语言: | English English |
| 出版: |
Wiley-VCH GmbH
2019
|
| 主题: | |
| 在线阅读: | https://eprints.ums.edu.my/id/eprint/31059/1/Graphite%20whiskers%20derived%20from%20waste%20coffee%20grounds%20treated%20at%20high%20temperature-ABSTRACT.pdf https://eprints.ums.edu.my/id/eprint/31059/2/Graphite%20whiskers%20derived%20from%20waste%20coffee%20grounds%20treated%20at%20high%20temperature.pdf https://eprints.ums.edu.my/id/eprint/31059/ https://onlinelibrary.wiley.com/doi/full/10.1002/gch2.201800107 https://doi.org/10.1002/gch2.201800107 |
| 标签: |
添加标签
没有标签, 成为第一个标记此记录!
|
| 总结: | Graphite whiskers (GWs) are obtained from coffee grounds (CGs) treated at 2500 °C for 1 h in the presence of Ar gas at 1 atm. The majority of the GWs formed inside the CGs shell are rod-like with a conical tip with diameter and length in the range between 1 to 3 µm and 4 to 10 µm, respectively. At first, the carbon layer might be grown in a turbostratic manner, and then progressively graphitized at higher temperature. The strong G′ peak intensity might be induced by the disclination of graphitized carbon layers. |
|---|