The effect of the cooling rate on the variant selection mechanism during bainite transformation was investigated in 2Cr- 1Mo steel. The specimen was heat treated to 1350 ℃ and held for 60s before being cooled to room temperature with various cooling rates. The usage of high temperature laser scannin...
保存先:
| 主要な著者: | , |
|---|---|
| フォーマット: | Non-Indexed Article |
| 出版事項: |
ARPN
2015
|
| オンライン･アクセス: | http://discol.umk.edu.my/id/eprint/8277/ http://www.arpnjournals.org/jeas/research_papers/rp_2015/jeas_1115_2899.pdf |
| タグ: |
タグ追加
タグなし, このレコードへの初めてのタグを付けませんか!
|
| 要約: | The effect of the cooling rate on the variant selection mechanism during bainite transformation was investigated in 2Cr-
1Mo steel. The specimen was heat treated to 1350 ℃ and held for 60s before being cooled to room temperature with
various cooling rates. The usage of high temperature laser scanning confocal microscopy (LSCM) to heat and cool the
specimen under controllable conditions enabled the bainite transformation to be observed in a real time. The heat treated
sample was then analyzed by using electron backscattered diffraction (EBSD) method. As a result, increasing the cooling
rate was discovered to refine the bainite block size. In the higher cooling rates, high angle variants were formed
prominently. |
|---|