Surface crack growth in a solid cylinder under combined cyclic bending-torsion loading

Here, we present fatigue crack growth (FCG) of a surface crack in a solid cylinder under combined cyclic torsionbending load. The effective stress intensity factors were found to be fluctuated during the crack growth. When the loading ratio of the maximum shearing stress over the maximum bending str...

Saved in:

书目详细资料
Main Authors:	Chandra, Devi, Purbolaksono, Judha, Yusoff, Nukman
格式:	Article
出版:	Asian Research Publishing Network 2018
主题:	TJ Mechanical engineering and machinery
在线阅读:	http://eprints.um.edu.my/22270/ http://www.arpnjournals.org/jeas/research_papers/rp_2018/jeas_0218_6771.pdf
标签:	添加标签没有标签, 成为第一个标记此记录!

相似书籍

Empirical solutions for stress intensity factors of a surface crack in a solid cylinder under pure torsion
由: Ramezani, Mohammadkazem, et al.
出版: (2018)

Fatigue growth analyses of a part-through crack in a solid bar under combined cyclic tension-torsion loading / Devi Chandra
由: Devi, Chandra
出版: (2016)

Stress intensity factors for embedded cracks within torsionally loaded square prismatic bars
由: Zhou, Ding, et al.
出版: (2019)

Stress intensity factors under combined bending and torsion moments
由: Al Emran, Ismail, et al.
出版: (2014)

Stress intensity factors under combined bending and torsion moments
由: Ismail, Al Emran, et al.
出版: (2012)

Modes I-II-III stress intensity factors of a semi-elliptical surface crack at a round bar under torsion loading by FEM and DBEM
由: Barrinaya, Muhammad Akbar, et al.
出版: (2022)

Interaction of External Surface Cracks on Thick Cylinders under Mode III Moment and Combined with Mode I Loading
由: O.M, Al-Moayed, et al.
出版: (2024)

Tetrahedral meshing for a slanted semi-elliptical surface crack at a solid cylinder
由: Teh, S., et al.
出版: (2021)

Interaction Assessment of Stress Intensity Factors of Surface Cracks on Thick Cylinders under Tension Force and Bending Moment
由: Al-Moayed, Omar Mohammed, et al.
出版: (2024)

Constraint Estimation Schemes For Semi-Elliptical Surface Cracks Under Tensile And Bending Loads
由: Latiff, Rizman Hariz Abdul
出版: (2017)

Surface Crack Analysis Under Cyclic Loads Using Probabilistic S-Version Finite Element Model
由: M. R. M., Akramin, et al.
出版: (2015)

J-integral analysis of surface cracks in round bars under combined loadings
由: A. Emran, Ismail, et al.
出版: (2014)

Torsional behaviour of RC box beams strengthened by CFRP under combined shear and torsion
由: Ma, Shengqiang, et al.
出版: (2022)

Stress intensity factors for surface cracks in round bar under single and combined loadings
由: Ismail, Al Emran, et al.
出版: (2012)

J-integral analysis of surface cracks in round bars under bending moments
由: A.E., Ismail, et al.
出版: (2014)

Closed-form solution for stress intensity factors of semi elliptical surface cracks with different inclinations in a cylinder bar under pure tension and pure torsion / Mohammadkazem Ramezani
由: Mohammadkazem, Ramezani
出版: (2018)

Behaviour of timber beams of different species under pure bending and pure torsion / Nordin Hassan
由: Hassan, Nordin
出版: (1981)

Crack behavior of heat treated sintered steel under cyclic loading / Al Emran Ismail
由: Ismail, Al Emran
出版: (2003)

Analysis of surface cracks in round bars using dual boundary element method
由: Ramezani, Mohammadkazem, et al.
出版: (2018)

Finite element analysis of j-integral for surface cracks in round bars under combined mode i loading
由: Ismail, Al Emran, et al.
出版: (2017)

Pre-tensioned steel straps for seismic retrofit of reinforced concrete columns under combined loading of flexure, shear and torsion
由: Tan, Jia Yang, et al.
出版: (2023)

Surface Roughness of Laser Modified Die Surface Change Under Thermal Cyclic Loading
由: Sheng, Annie Lau, et al.
出版: (2019)

Crack length dependence of mode III delamination using edge crack torsion test
由: Wong, K. J., et al.
出版: (2017)

Stress intensity factors for embedded cracks within torsionally loaded square prismatic bars / Zhou Ding
由: Zhou, Ding
出版: (2017)

Characterization of rubber degradation in a brake wheel cylinder under cyclic loading / Abdul Hakim Abdullah ... [et al.]
由: Abdullah, Abdul Hakim, et al.
出版: (2023)

Comparative study on bending and torsional effect of highly thermal graphene hybridization conductive ink
由: Ismail, Ismaniza
出版: (2023)

Design and fabrication of bending machine for torsion test specimen preparation / Mohamad Sufian Ahmad
由: Ahmad, Mohamad Sufian
出版: (2023)

Simulation of crack under compression loads.
由: Ali, Aidy, et al.
出版: (2009)

Prediction of Fatigue Crack Growth for Semi-Elliptical Surface Cracks using S-version Fem under Tension Loading
由: M. S., Shaari, et al.
出版: (2016)

J-integral analysis of surface cracks in round bars under tension loadings
由: A. Emran, Ismail, et al.
出版: (2014)

ENDURANCE INVESTIGATION OF NITRIDE FERRITIC STAINLESS STEEL SS439 UNDER TORSIONAL LOADING
由: Mohammad Latpi, Aliff Idham
出版: (2013)

Ratcheting behaviour of aluminum under cyclic axial load
由: Low, Chiang Wooi
出版: (2012)

Young's modulus of peat soil under cyclic loading
由: Habib Musa Mohamad, et al.
出版: (2021)

Statically-Indeterminate SFRC Columns under Cyclic Loads
由: Abbas, Ali A., et al.
出版: (2014)

Torsional behaviours and crack localization in palm oil clinker concrete / Safdar Khan
由: Safdar, Khan
出版: (2021)

Exact solution for stresses/displacements in a multilayered hollow cylinder under thermo-mechanical loading
由: Yeo, W.H., et al.
出版: (2017)

Inelastic responses of swollen nitrile rubber under cyclic loading
由: Loo, Mei Sze, et al.
出版: (2018)

Cohesive zone modelling of mode III delamination using the edge crack torsion test
由: Israr, H. A., et al.
出版: (2017)

Torsional and cracking characteristics of steel fiber-reinforced oil palm shell lightweight concrete
由: Yap, Soon Poh, et al.
出版: (2016)

Torsional crack localization in palm oil clinker concrete using acoustic emission method
由: Khan, Safdar, et al.
出版: (2021)