Preparation and characterization of plasticized ethylene carbonate (EC) on cellulose- NH4I electrolyte / Marini Musataffa.
In this study, cellulose acetate (CA) containing different concentration of ammonium iodide (NH4I) salt were prepared using a solution cast technique. The optimum percentage of salt and plasticizer that gave the highest value of electrical conductivity of the sample was determined. Impedance spectro...
保存先:
| 第一著者: | |
|---|---|
| フォーマット: | Student Project |
| 言語: | English |
| 出版事項: |
2008
|
| 主題: | |
| オンライン･アクセス: | https://ir.uitm.edu.my/id/eprint/46749/1/46749.pdf https://ir.uitm.edu.my/id/eprint/46749/ |
| タグ: |
タグ追加
タグなし, このレコードへの初めてのタグを付けませんか!
|
| 要約: | In this study, cellulose acetate (CA) containing different concentration of ammonium iodide (NH4I) salt were prepared using a solution cast technique. The optimum percentage of salt and plasticizer that gave the highest value of electrical conductivity of the sample was determined. Impedance spectroscopy technique was carried out in order to determine the electrical conductivity value. The highest conductivity value was 3.7515xl0-5 Scm-1 for 1 g CA at 35 wt % ammonium iodide at 303 K. This conductivity was calculated using the bulk resistance value which can be obtained from the complex impedance plot in frequency range between 100 Hz and 1 MHz. The same procedure was repeated in order to prepare plasticized samples with ethylene carbonate (EC) using the optimum concentration of salted sample. The highest conductivity was 3.4396x10-4 Scm-1 at 40 wt % EC. Finally, the highest conducting plasticized sample was characterized using impedance spectroscopy at different temperatures from 303K to 373K. |
|---|