Preparation and characterization of plasticized ethylene carbonate (EC) on cellulose- NH4I electrolyte / Marini Musataffa.
In this study, cellulose acetate (CA) containing different concentration of ammonium iodide (NH4I) salt were prepared using a solution cast technique. The optimum percentage of salt and plasticizer that gave the highest value of electrical conductivity of the sample was determined. Impedance spectro...
Saved in:
| 主要作者: | |
|---|---|
| 格式: | Student Project |
| 语言: | English |
| 出版: |
2008
|
| 主题: | |
| 在线阅读: | https://ir.uitm.edu.my/id/eprint/46749/1/46749.pdf https://ir.uitm.edu.my/id/eprint/46749/ |
| 标签: |
添加标签
没有标签, 成为第一个标记此记录!
|
| 总结: | In this study, cellulose acetate (CA) containing different concentration of ammonium iodide (NH4I) salt were prepared using a solution cast technique. The optimum percentage of salt and plasticizer that gave the highest value of electrical conductivity of the sample was determined. Impedance spectroscopy technique was carried out in order to determine the electrical conductivity value. The highest conductivity value was 3.7515xl0-5 Scm-1 for 1 g CA at 35 wt % ammonium iodide at 303 K. This conductivity was calculated using the bulk resistance value which can be obtained from the complex impedance plot in frequency range between 100 Hz and 1 MHz. The same procedure was repeated in order to prepare plasticized samples with ethylene carbonate (EC) using the optimum concentration of salted sample. The highest conductivity was 3.4396x10-4 Scm-1 at 40 wt % EC. Finally, the highest conducting plasticized sample was characterized using impedance spectroscopy at different temperatures from 303K to 373K. |
|---|